Volume Stability and Mechanical Properties of Cement Paste Containing Natural Fibers from Phragmites-Australis Plant at Elevated Temperature

The utilization of bio-fiber materials in building components has become imperative for improving sustainability, controlling global warming, addressing environmental concerns, and enhancing concrete properties. This study is part of a wide-range investigation on the use of Phragmites-Australis (PhA) fibers in construction and building materials. In this paper, the volume stability and mechanical properties of paste containing PhA fibers and exposed to high temperatures were investigated. Four mixes were made with 0, 0.5, 1, and 2% fibers by volume. To evaluate the volume stability and mechanical properties, the chemical shrinkage, autogenous shrinkage, drying shrinkage, expansion, ultrasonic pulse velocity, compressive strength, and flexural strength were tested. The curing duration and temperature were 180 days and 45 °C, respectively. The results indicated that an addition of PhA fibers of up to 2% resulted in a reduction in all the shrinkage parameters at 180 days. The presence of PhA fibers in the paste tended to reduce the compressive strength, with the lowest value observed at 2%. Apart from the values at 90 days, the optimal flexural strength seemed to be achieved by the paste with 1% PhA fibers. To further elucidate the experimental results, a hyperbolic model was employed to predict the variation in the length change as a function of the curing age with a high accuracy. Based on the results obtained, PhA fibers can play a crucial role in mitigating the shrinkage parameters and enhancing the mechanical properties of cement paste.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.