Analyzing the early structural build-up of accelerated cement pastes

Extrusion-based additive manufacturing imposes high requirements on the material stability right after the extrusion. Therefore, a thorough understanding of the chemical reactions that determine the early reduction in processability is necessary. Accelerators are especially considered here, which have a major influence on the early reaction. This study contributes to these issues by analyzing the influence of 0.1 wt% TEA (triethanolamine) and 2.0 wt% Ca(NO₃)₂on the hydration of two CEM I 52.5 R. The hydration was analyzed by isothermal heat flow calorimetry and in-situ X-ray diffraction. Vicat needle penetration, a penetrometer of own design, and ultrasonic P-wave velocity development were used to monitor the early change in workability. The obtained results indicate that ettringite formation is the main factor influencing workability during the first 60 min of hydration. Afterwards, the influence of ettringite is exceeded by the formation of C–S–H. Ca(NO₃)₂was shown to enhance C–S–H formation and had no significant effect on the workability during the first 60 min of hydration while rapidly decreasing workability during the induction period. TEA was shown to increase brownmillerite dissolution and ettringite formation and, consequently, promote the workability loss during the initial hydration period. The time of initial and final setting determined by the Vicat needle test depended mainly on the formation of C–S–H phases.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.