The Effect of Activators on the Mechanical Properties and Microstructure of Alkali-Activated Nickel Slag

In order to mitigate problems associated with environmental pollution, alkali-activated nickel slags (AANSs) may be used as an alternative to cementitious material. However, the understanding of their mechanical properties and microstructure is currently very limited. This paper therefore explores the influence of different types and contents of three solid alkali activators, Na₂SiO₃, NaOH, and Na₂SiO₃/Na₂CO₃, on the compressive strength of one-part AANS. Their microstructure, hydration components, and pore structure are analyzed by means of a scanning electron microscope, an energy-dispersive spectrometer, an X-ray diffractometer, an infrared spectrometer, and a mercury analyzer. The results show that the AANS with an Na₂SiO₃/Na₂CO₃activator has a denser microstructure, lower porosity, and a smaller pore size when compared with the AANS with the Na₂SiO₃or NaOH activators. Consequently, the compressive strength of the Na₂SiO₃/Na₂CO₃sample reached a higher compressive strength (96 MPa) than that activated by Na₂SiO₃or NaOH. This strength is optimal as well as more economical as Na₂O, which increased from 0.107 mol to 0.123 mol, contributes little to compressive strength. The final part of the article discusses an optimal design for the engineering application of one-part AANS.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.